Condensed Matter > Materials Science
[Submitted on 8 May 2006]
Title:Transmission electron microscopy investigation of segregation and critical floating-layer content of indium for island formation in InGaAs
View PDFAbstract: We have investigated InGaAs layers grown by molecular-beam epitaxy on GaAs(001) by transmission electron microscopy (TEM) and photoluminescence spectroscopy. InGaAs layers with In-concentrations of 16, 25 and 28 % and respective thicknesses of 20, 22 and 23 monolayers were deposited at 535 C. The parameters were chosen to grow layers slightly above and below the transition between the two- and three-dimensional growth mode. In-concentration profiles were obtained from high-resolution TEM images by composition evaluation by lattice fringe analysis. The measured profiles can be well described applying the segregation model of Muraki et al. [Appl. Phys. Lett. 61 (1992) 557]. Calculated photoluminescence peak positions on the basis of the measured concentration profiles are in good agreement with the experimental ones. Evaluating experimental In-concentration profiles it is found that the transition from the two-dimensional to the three-dimensional growth mode occurs if the indium content in the In-floating layer exceeds 1.1+/-0.2 monolayers. The measured exponential decrease of the In-concentration within the cap layer on top of the islands reveals that the In-floating layer is not consumed during island formation. The segregation efficiency above the islands is increased compared to the quantum wells which is explained tentatively by strain-dependent lattice-site selection of In. In addition, In0.25Ga0.75As quantum wells were grown at different temperatures between 500 oC and 550 oC. The evaluation of concentration profiles shows that the segregation efficiency increases from R=0.65 to R=0.83.
References & Citations
Bookmark
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Connected Papers (What is Connected Papers?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
alphaXiv (What is alphaXiv?)
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Hugging Face (What is Huggingface?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
CORE Recommender (What is CORE?)
IArxiv Recommender
(What is IArxiv?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.