Title:Structural and Electrical Transport Properties of NASICON type Na$_{3}$Zr$_{2-x}$Ti$_{x}$Si$_2$PO$_{\rm 12}$ ($x=$ 0.1-0.4) Solid Electrolyte Materials
View PDF HTML (experimental)Abstract:We report the structural, resistivity, impedance, and dielectric studies of isovalent substituted Na$_{3}$Zr$_{2-x}$Ti$_{x}$Si$_2$PO$_{\rm 12}$ ($x=$ 0.1--0.4) NASICON type solid electrolyte materials. The Rietveld refinement of XRD patterns shows the monoclinic phase with space group of C 2/c for all the samples. The resistivity analysis shows the Arrhenius-type thermal conduction with an increase in activation energy with doping is explained based on decreased unit cell volume. We use Maxwell-Wagner-Sillars (MWS) relaxation and space charge or interfacial polarization models to explain the frequency and temperature-dependent variations of electric permittivity. The double relaxation peaks in the dielectric loss data show the two types of relaxation mechanisms of different activation energy. The real ($\epsilon^{'}$) and imaginary ($\epsilon^{''}$) parts of permittivity are fitted using the modified Cole-Cole equation, including the conductivity term, which show the non-Debye type relaxation over the measured frequency and temperature range. The impedance analysis shows the contributions from grain and grain boundary relaxation. The fitting performed using the impedance and constant-phase element (CPE) confirm the non-Debye type relaxation. Moreover, the electric modulus analysis confirms the ionic nature having thermally activated relaxation and the modulus scaling analysis shows a similar type of relaxation in the measured temperature range. The modified power law is used to understand the frequency dependence of {\it a.c.} conductivity data. The temperature dependence of exponent ($s$) in modified power law suggests the change in the conduction mechanism from near small polaron tunneling (NSPT) to correlated barrier hopping (CBH) above room temperature. The larger values of $\epsilon$$_{r}$ indicate these materials as a potential candidate for charge-storage devices.
Submission history
From: Rajendra S. Dhaka [view email][v1] Tue, 8 Apr 2025 09:36:05 UTC (1,484 KB)
Current browse context:
cond-mat.mtrl-sci
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Connected Papers (What is Connected Papers?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
alphaXiv (What is alphaXiv?)
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Hugging Face (What is Huggingface?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
CORE Recommender (What is CORE?)
IArxiv Recommender
(What is IArxiv?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.