Title:Mutual control of critical temperature, RRR, stress, and surface quality for sputtered Nb films

Abstract:Superconducting single quantum logic integrated circuits traditionally exploit magnetron sputtered niobium thin films on silicon oxide substrates. The sputtering depends on multiple process parameters, which dramatically affect mechanical, electrical, and cryogenic properties of Nb thin films. In this work, we focus on the comprehensive relationship study between 200-nm Nb film characteristics and their intrinsic stress. It is shown that there is a critical value of the working pressure pcritical at the fixed sputtering power above which stress in the film relaxes whereas the film properties degrade significantly. Below pcritical one can control intrinsic stress in the wide range from -400 MPa to +600 MPa maintaining perfect film surface with a 0.8 nm roughness (Rq), electrical resistivity less than 20 uOhm*cm, critical superconducting transition temperature above 8.9 K and residual resistance ratio over 6.4. We suggest a modified kinetic model to predict Nb films stress with the linear dependence of high-energy parameters on the working pressure replaced with an exponential one, which allowed reduction of the approximation error from 20 to 8%.