Title:Fatigue life prediction at mesoscopic scale of samples containing casting defects: A novel energy based non-local model
View PDF HTML (experimental)Abstract:Fatigue failure driven by stress gradients associated to casting defects was studied in two cast nickel-based superalloys. The experimental campaign revealed complex damage phenomena linked to spongeous shrinkages, characterized by their intricate arrangement of defects in the material medium, forming defect clusters. Multiple cracks were observed to initiate from defect volumes, coalescing with neighboring void surfaces along crystallographic planes. Defects were characterized using X-ray computed tomography, and image-based finite element (FE) models were constructed as digital representations of each experimental sample explicitly containing all real casting defects. Numerical simulations of these FE models under the same conditions as the experiments revealed that tortuous defects contain small ligaments where very high local stresses develop. These ligaments initiate early cracks, but due to the limited stressed volumes, these cracks do not drive the life of the material. A thorough comparison of simulations with experiments led to the development of an original method to define stressed volumes and address small ligaments. Finally, a novel energy-based non-local model was proposed, using two parameters to predict the fatigue lives of samples containing casting defects at the mesoscopic scale. The model was validated against samples with varying porosity levels, sizes, and geometries, accurately predicting fatigue lives within a factor of 3 compared to experimental results. This new approach generalizes the application of non-local methods to real casting defects by considering their shape and stressed volumes to estimate fatigue properties.
Current browse context:
physics.app-ph
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
Connected Papers (What is Connected Papers?)
CORE Recommender (What is CORE?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.