Title:Ultrafast high-temperature sintering of dense and textured alumina
View PDFAbstract:Crystallographic texture engineering in ceramics is essential to achieve direction-specific properties. Current texture engineering methods are time-consuming, energy extensive, or can lead to unnecessary diffusion of added dopants. Herein, we explore ultrafast high-temperature sintering (UHS) to prepare dense and textured alumina using templated grain growth (TGG). From a slurry containing alumina microplatelets coated with Fe3O4 nanoparticles dispersed in a matrix of alumina nanoparticles, green bodies with oriented microplatelets were prepared using magnetic assisted slip casting (MASC). The effects of the sintering temperature, time and heating rate on the density and microstructure of the obtained ceramics were then studied. We found that TGG occurs for a temperature range between 1640 and 1780 °C and 10 s sintering time. Sintering at 1700 °C for 10 s led to dense and textured alumina with anisotropic grains thanks to the Fe3O4 coating, which did not have the time to diffuse. The highest texture and relative density were obtained with a heating rate of ~5,500 °C/min, leading to texture-dependent anisotropic mechanical properties. This study opens new avenues for fabricating textured ceramics in ultra-short times.
Submission history
From: Rohit Pratyush Behera Dr. [view email][v1] Fri, 28 Jun 2024 23:03:06 UTC (3,343 KB)
Current browse context:
cond-mat.mtrl-sci
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
Connected Papers (What is Connected Papers?)
CORE Recommender (What is CORE?)
IArxiv Recommender
(What is IArxiv?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.