Title:Zeta potential and nanodiamond self assembly assisted diamond growth on lithium niobate and lithium tantalate single crystal

Authors:Soumen Mandal, Karsten Arts, David Morgan, Zhuohui Chen, Oliver A. Williams
View PDF
Abstract:This study focuses on the self-assembly and subsequent diamond growth on SiO$_2$ buffered lithium niobate (LiNbO$_3$) and lithium tantalate (LiTaO$_3$) single crystals. The zeta-potential of LNO and LTO single crystal were measured as a function of pH. They were found to be negative in the pH range 3.5-9.5. The isoelectric point for LNO was found to be at pH $\sim$ 2.91 and that of LTO to be at pH $\sim$ 3.20. X-ray photoelectron spectroscopy performed on the surfaces show presence of oxygen groups which may be responsible for the negative zeta potential of the crystals. Self-assembly of nanodiamond particles on LTO and LNO, using nanodiamond colloid, were studied. As expected, high nanodiamond density was seen when self-assembly was done using a positively charged nanodiamond particles. Diamond growth was attempted on the nanodiamond coated substrates but they were found to be unsuitable for direct growth due to disintegration of substrates in diamond growth conditions.. A $\sim$100nm thick silicon dioxide layer was deposited on the crystals, followed by nanodiamond self assembly and diamond growth. Thin diamond films were successfully grown on both coated crystals. The diamond quality was analysed by Raman spectroscopy and atomic force microscopy.
Subjects: Materials Science (cond-mat.mtrl-sci); Applied Physics (physics.app-ph)
Cite as: arXiv:2305.08652 [cond-mat.mtrl-sci]
  (or arXiv:2305.08652v1 [cond-mat.mtrl-sci] for this version)
  https://doi.org/10.48550/arXiv.2305.08652

Submission history

From: Soumen Mandal [view email]
[v1] Mon, 15 May 2023 13:53:27 UTC (14,348 KB)
Full-text links:

Access Paper:

  • View PDF
  • TeX Source
  • Other Formats
license icon view license
Current browse context:
cond-mat.mtrl-sci
< prev   |   next >
new | recent | 2023-05
Change to browse by:
cond-mat
physics
physics.app-ph

References & Citations

export BibTeX citation

Bookmark

BibSonomy logo Reddit logo

Bibliographic and Citation Tools

Bibliographic Explorer (What is the Explorer?)
Connected Papers (What is Connected Papers?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)

Code, Data and Media Associated with this Article

alphaXiv (What is alphaXiv?)
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Hugging Face (What is Huggingface?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)

Demos

Replicate (What is Replicate?)
Hugging Face Spaces (What is Spaces?)
TXYZ.AI (What is TXYZ.AI?)

Recommenders and Search Tools

Influence Flower (What are Influence Flowers?)
CORE Recommender (What is CORE?)
IArxiv Recommender (What is IArxiv?)

arXivLabs: experimental projects with community collaborators

arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.

Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.

Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.

Which authors of this paper are endorsers? | Disable MathJax (What is MathJax?)