Title:Impact of Trap Filling on Carrier Diffusion in MAPbBr$_3$ Single Crystals
View PDFAbstract:We present experimental evidence showing that the effective carrier diffusion length ($L_d$) and lifetime ($\tau$) depend on the carrier density in MAPbBr$_3$ single crystals. Independent measurements reveal that both $L_d$ and $\tau$ decrease with an increase in photo-carrier density. Scanning photocurrent microscopy is used to extract the characteristic photocurrent $I_{ph}$ decay-length parameter, $L_d$, which is a measure of effective carrier diffusion. The $L_d$ magnitudes for electrons and holes were determined to be ~ 13.3 $\mu$m and ~ 13.8 $\mu$m respectively. A marginal increase in uniform light bias ($\leq 5 \times 10^{15}$ photons/cm$^2$) increases the modulated photocurrent magnitude and reduces the $L_d$ parameter by a factor of two and three for electrons and holes respectively, indicating that the recombination is not monomolecular. The $L_d$ variations were correlated to the features in photoluminescence lifetime studies. Analysis of lifetime variation shows intensity-dependent monomolecular and bimolecular recombination trends with recombination constants determined to be ~ 9.3 $\times 10^6$ s$^{-1}$ and ~ 1.4 $\times 10^{-9}$ cm$^{3}$s$^{-1}$ respectively. Based on the trends of $L_d$ and lifetime, it is inferred that the sub-band-gap trap recombination influences carrier transport in the low-intensity excitation regime, while bimolecular recombination and transport dominate at high intensity.
Current browse context:
physics.app-ph
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Connected Papers (What is Connected Papers?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
alphaXiv (What is alphaXiv?)
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Hugging Face (What is Huggingface?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
CORE Recommender (What is CORE?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.