Title:Measurements with silicon detectors at extreme neutron fluences
View PDFAbstract:Thin pad detectors made from 75 $\mu$m thick epitaxial silicon on low resistivity substrate were irradiated with reactor neutrons to fluences from 2.5$\times 10^{16}$ n/cm$^2$ to 1$\times 10^{17}$ n/cm$^2$. Edge-TCT measurements showed that the active detector thickness is limited to the epitaxial layer and does not extend into the low resistivity substrate even after the highest fluence. Detector current was measured under reverse and forward bias. The forward current was higher than the reverse at the same voltage but the difference gets smaller with increasing fluence. Rapid increase of current (breakdown) above ~ 700 V under reverse bias was observed. An annealing study at 60$^\circ$C was made to 1200 minutes of accumulated annealing time. It showed that the reverse current anneals with similar time constants as measured at lower fluences. A small increase of forward current due to annealing was seen. Collected charge was measured with electrons from $^{90}$Sr source in forward and reverse bias configurations. Under reverse bias the collected charge increased linearly with bias voltage up to 6000 electrons at 2.5$\times 10^{16}$ n/cm$^2$ and 3000 electrons at 1$\times 10^{17}$ n/cm$^2$. Rapid increase of noise was measured above $\sim$ 700 V reverse bias due to breakdown resulting in worse S/N ratio. At low bias voltages slightly more charge is measured under forward bias compared to reverse. However better S/N is achieved under reverse bias. Effective trapping times were estimated from charge collection measurements under forward bias showing that at high fluences they are much longer than values extrapolated from low fluence measurements - at 1$\times 10^{17}$ n/cm$^2$ a factor of 6 larger value was measured.
Submission history
From: Igor Mandić [view email][v1] Fri, 10 Jul 2020 14:44:47 UTC (7,643 KB)
[v2] Mon, 13 Jul 2020 14:44:33 UTC (4,693 KB)
[v3] Wed, 2 Sep 2020 08:56:03 UTC (4,694 KB)
Current browse context:
physics.ins-det
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Connected Papers (What is Connected Papers?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
alphaXiv (What is alphaXiv?)
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Hugging Face (What is Huggingface?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
CORE Recommender (What is CORE?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.