Title:Trapping of solute atoms at grain boundaries in GdNi2
View PDFAbstract:Lattice locations of 111In impurity probe atoms in intermetallic GdNi2 were studied as a function of alloy composition and temperature using perturbed angular correlation spectroscopy (PAC). Three nuclear quadrupole interaction signals were detected and their equilibrium site fractions were measured up to 700 oC. Two signals have well-defined electric field gradients (EFGs) and are attributed to In-probes on Gd- and Ni-sites in a well-ordered lattice. A third, inhomogeneously broadened signal was observed at low temperature. This is attributed to trapping, or segregation, of In-probes to lattice sinks such as grain boundaries (GB) that have a large multiplicity of local environments and EFGs. Changes in site fractions were reversible above 300oC. Measurements were made on a pair of samples that were richer and poorer in Gd. Remarkably, the GB-site was populated only in the more Gd-rich sample. This is explained by the hypothesis that excess Gd segregates to the grain boundaries and provides a lower enthalpy environment for In-probe atoms. Observations are discussed in relation to a three-level quantum system. Enthalpy differences between levels were determined from measurements of temperature dependences of ratios of site fractions. The enthalpy of transfer of In-probes from the Gd- to Ni-sublattice was found to be much smaller in the Gd-rich sample. This is attributed to a large temperature-dependence in the degeneracies of levels available to In-solutes in the phase, leading to an effective transfer enthalpy that differs greatly from the difference in site-enthalpies. A possible scenario is discussed. Different segregation enthalpies were measured for In-solute transferring from GB sites to Gd- and Ni-sites, whereas only an average value can be determined through macroscopic measurements.
Current browse context:
cond-mat.mtrl-sci
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Connected Papers (What is Connected Papers?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
alphaXiv (What is alphaXiv?)
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Hugging Face (What is Huggingface?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
CORE Recommender (What is CORE?)
IArxiv Recommender
(What is IArxiv?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.