Title:Mobility Improvement and Temperature Dependence in MoSe2 Field-Effect Transistors on Parylene-C Substrate
View PDFAbstract:We report low temperature scanning tunneling microscopy characterization of MoSe2 crystals, and the fabrication and electrical characterization of MoSe2 field-effect transistors on both SiO2 and parylene-C substrates. We find that the multilayer MoSe2 devices on parylene-C show a room temperature mobility close to the mobility of bulk MoSe2 (100 cm2V-1s-1 - 160 cm2V-1s-1), which is significantly higher than that on SiO2 substrate (~50 cm2V-1s-1). The room temperature mobility on both types of substrates are nearly thickness independent. Our variable temperature transport measurements reveal a metal-insulator transition at a characteristic conductivity of e2/h. The mobility of MoSe2 devices extracted from the metallic region on both SiO2 and parylene-C increases up to ~ 500 cm2V-1s-1 as the temperature decreases to ~ 100 K, with the mobility of MoSe2 on SiO2 increasing more rapidly. In spite of the notable variation of charged impurities as indicated by the strongly sample dependent low temperature mobility, the mobility of all MoSe2 devices on SiO2 converges above 200 K, indicating that the high temperature (> 200 K) mobility in these devices is nearly independent of the charged impurities. Our atomic force microscopy study of SiO2 and parylene-C substrates further rule out the surface roughness scattering as a major cause of the substrate dependent mobility. We attribute the observed substrate dependence of MoSe2 mobility primarily to the surface polar optical phonon scattering originating from the SiO2 substrate, which is nearly absent in MoSe2 devices on parylene-C substrate.
Current browse context:
cond-mat.mtrl-sci
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Connected Papers (What is Connected Papers?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
alphaXiv (What is alphaXiv?)
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Hugging Face (What is Huggingface?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
CORE Recommender (What is CORE?)
IArxiv Recommender
(What is IArxiv?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.