Title:Interplane resistivity of underdoped single crystals (Ba$_{1-x}$K$_x$)Fe$_2$As$_2$, $0 \leq x<0.34$
View PDFAbstract:Temperature-dependent inter-plane resistivity, $\rho _c(T)$, was measured in hole-doped iron-arsenide superconductor (Ba$_{1-x}$K$_x$)Fe$_2$As$_2$ over a doping range from parent compound to optimal doping $T_c\approx 38~K$, $0\leq x \leq 0.34$. Measurements were undertaken on high-quality single crystals grown from FeAs flux. The coupled magnetic/structural transition at $T_{SM}$ leads to clear accelerated decrease of $\rho_c(T)$ on cooling in samples with $T_c <$26~K ($x <0.25$). This decrease in hole-doped material is in notable contrast to an increase in $\rho_c(T)$ in the electron-doped Ba(Fe$_{1-x}$Co$_x$)Fe $_2$As$_2$ and iso-electron substituted BaFe$_2$(As$_{1-x}$P$_x$)$_2$. The $T_{SM}$ decreases very sharply with doping, dropping from $T_s$=71~K to zero on increase of $T_c$ from approximately 25 to 27~K. The $\rho_c(T)$ becomes $T$-linear close to optimal doping. The broad crossover maximum in $\rho_c(T)$, found in the parent BaFe$_2$As$_2$ at around $T_{max} \sim$200~K, shifts to higher temperature $\sim$250~K with doping $x$=0.34. The maximum shows clear correlation with the broad crossover feature found in the temperature-dependent in-plane resistivity $\rho_a(T)$. The doping evolution of $T_{max}$ in (Ba$_{1-x}$K$_x$)Fe$_2$As$_2$ is in notable contrast with both rapid suppression of $T_{max}$ found in Ba(Fe$_{1-x}TM_x$)$_2$As$_2$ ($TM$=Co,Rh,Ni,Pd) and its rapid increase BaFe$_2$(As$_{1-x}$P$_x$)$_2$. This observation suggest that pseudogap features are much stronger in hole-doped than in electron-doped iron-based superconductors, revealing significant electron-hole doping asymmetry similar to the cuprates. This paper replaces: cond-mat:1106.0533.
Current browse context:
cond-mat.supr-con
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Connected Papers (What is Connected Papers?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
alphaXiv (What is alphaXiv?)
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Hugging Face (What is Huggingface?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
CORE Recommender (What is CORE?)
IArxiv Recommender
(What is IArxiv?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.