Condensed Matter > Strongly Correlated Electrons
[Submitted on 1 Feb 2014]
Title:Anisotropic magnetic properties and giant magnetocaloric effect of PrSi single crystal
View PDFAbstract:Single crystal of PrSi was grown by Czochralski method in a tetra-arc furnace. Powder x-ray diffraction of the as grown crystal revealed that PrSi crystallizes in FeB$-$type structure with space group $Pnma$ (no. 62). PrSi undergoes a ferromagnetic transition at 52 K with [010] direction as the easy axis of magnetization. Heat capacity data confirm the bulk nature of the transition at 52 K and exhibit a huge anomaly at the transition. A sharp rise in the low temperature heat capacity has been observed (below 5 K) which is attributed to the $^{141}$Pr nuclear Schottky heat capacity arising from the hyperfine field of the Pr moment. The estimated Pr magnetic moment 2.88 $\mu_{\rm B}$/Pr from the hyperfine splitting is in agreement with the saturation magnetization value obtained from the magnetization data measured at 2 K. From the crystal electric field (CEF) analysis of the magnetic susceptibility, magnetization and the heat capacity data it is found that the degenerate $J = 4$ Hund's rule derived state of Pr$^{3+}$-ion splits into nine singlets with an overall splitting of 284 K, the first excited singlet state separated by just 9 K from the ground state. The magnetic ordering in PrGe appears to be due to the exchange generated admixture of low lying crystal field levels. Magnetocaloric effect (MCE) has been investigated from magnetization data along all the three principal crystallographic directions. Large magnetic entropy change, $-\Delta S_M = $22.2 J/kg K, and the relative cooling power, RCP = $460$ J/kg, characteristic of giant magneto caloric effect are achieved near the transition temperature ($T_{\rm C}$ = 52 K) for $H =$~70 kOe along $[010]$. Furthermore, the PrSi single crystal exhibits a giant MCE anisotropy.
Submission history
From: Arumugam Thamizhavel [view email][v1] Sat, 1 Feb 2014 16:00:01 UTC (3,206 KB)
Current browse context:
cond-mat.str-el
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
Connected Papers (What is Connected Papers?)
CORE Recommender (What is CORE?)
IArxiv Recommender
(What is IArxiv?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.