Title:Effect of hydrostatic pressure on elastic properties of ZDTP tribofilms
View PDFAbstract: Previous studies have shown that the elastic properties of Zinc Dialkyl-dithiophosphate (ZDTP) tribofilms measured by nanoindentation increase versus applied pressure (Anvil effect) [1, 2]. The aim of this paper is to demonstrate that, up to 8 GPa, this increase is a reversible phenomenon. A ZDTP tribofilm has been produced on "AISI 52100" steel substrate using a Cameron-Plint tribometer. After its formation, a hydrostatic pressure of about 8 GPa was applied during one minute on the tribofilm using a large radius steel ball ("Brinell-like" test). Nanoindentation tests were performed with a Berkovich tip on pads in order to measure and compare the mechanical properties of the tribofilm inside and outside the macroscopic plastically deformed area. Careful AFM observations have been carried out on each indent in order to take into account actual contact area. No difference in elastic properties was observed between the two areas: tribofilm modulus and pressure sensitivity are the same inside and outside the residual hemispherical print. This demonstrates that Anvil effect is a reversible phenomenon in the studied pressure range.
Submission history
From: Sandrine Bec [view email] [via CCSD proxy][v1] Thu, 28 Jun 2007 13:50:00 UTC (256 KB)
Current browse context:
physics.class-ph
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Connected Papers (What is Connected Papers?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
alphaXiv (What is alphaXiv?)
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Hugging Face (What is Huggingface?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
CORE Recommender (What is CORE?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.