Title:Structural stability, elemental ordering, and transport properties of layered ScTaN2

Abstract:Some ternary TM nitrides are predicted to adopt layered structures that make them interesting for thermoelectric conversion and quantum materials applications. Synthesis of TM ternary nitride films by physical vapor deposition often favors disordered 3D structures rather than the predicted 2D-like layered structure. In this study, we investigate the structural interplay in the Sc-Ta-N material system, focusing on ScTaN2. We use a two-step combinatorial approach to deposit Sc-Ta-N films by RF co-sputtering and then process the resulting 3D-structured precursor with RTA. Synchrotron GIWAXS on films annealed at 1200 °C for 20 min reveals the nucleation of the layered structure (P63/mmc) within a composition window of Sc/(Sc+Ta) = 0.2-0.5. We estimate the long-range order parameter in stoichiometric ScTaN2 films to be 0.86, corresponding to a fraction of antisites of 7%. Interestingly, we find that the structure can accommodate large off-stoichiometry in the Ta-rich region (x < 0.5), facilitated by making an alloy with the nearly isostructural Ta5N6 compound that exists on a composition tie-line. Transport measurements on ScTaN2 reveal a nearly temperature-independent high carrier density (1021 cm-3), suggesting a heavily doped semiconductor or semimetallic character. The carrier mobility is relatively small (9.5 cm2V-1s-1 at 2 K) and the residual-resistivity ratio is small, suggesting that electrical conduction is dominated by defects or disorder. Measured magnetoresistance is indicative of weak antilocalization at low temperatures. We highlight the interplay between ScTaN2 and Ta5N6 in stabilizing layered structures, emphasizes the importance of cation order/disorder for potential tunable alloys, and suggests that ScTaN2 is promising platform for exploring electronic properties in a tie line of stoichiometry.