Physics > Applied Physics
[Submitted on 3 Jan 2025]
Title:Landau-Levich Scaling for Optimization of Quantum Dot Layer Morphology and Thickness for Enhanced Quantum-Dot Light-Emitting Diode Performance
View PDFAbstract:Quantum dot (QD) light-emitting diodes (QLEDs) are promising candidates for next-generation displays because of their high efficiency, brightness, broad color gamut, and solution-processability. Large-scale solution-processing of electroluminescent QLEDs poses significant challenges, particularly concerning the precise control of the active layer's thickness and uniformity. These obstacles directly impact charge transport, leading to current leakage and reduced overall efficiency. Blade-coating is a prevalent and scalable solution processing technique known for its speed and minimal waste. Additionally, it allows for continuous "roll-to-roll" processing, making it highly adaptable in various applications. In this study, we demonstrate the precise control of blade speed in the Landau-Levich regime to create a uniform QD emission layer, using a commercial CdSe/ZnS QD as a representative example. QDs assemble into different morphologies on glass and the underlying layers of the QLED device due to variations in interaction energy. The QD film thickness can be modified from monolayer to multilayer by adjusting blade speed, which can be predicted by fitting the Landau-Levich-Derjaguin theory. The optimal speed at 7 mm/s results in a QD film with a surface coverage of around 163% and low roughness (1.57 nm mean square height). The QLED external quantum efficiency (EQE) of approximately 1.5% was achieved using commercially available CdSe/ZnS QDs with low photoluminescence quantum yield (PLQY), and an EQE of around 7% has been obtained using lab-made InP/ZnSe/ZnS QDs having a solution PLQY of 74%. All-blade-coated CdSe-QLEDs are further demonstrated by adopting the optimized speed for the QD layer. This method demonstrates significant potential for developing low-cost, reproducible, and scalable QLED technologies with uniform emission characteristics and low-waste production.
Current browse context:
cond-mat.mtrl-sci
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Connected Papers (What is Connected Papers?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
alphaXiv (What is alphaXiv?)
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Hugging Face (What is Huggingface?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
CORE Recommender (What is CORE?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.