Title:Targeting low micro-roughness for 3D printed aluminium mirrors using a hot isostatic press
View PDF HTML (experimental)Abstract:Additive manufacturing (AM; 3D printing) in aluminium using laser powder bed fusion provides a new design space for lightweight mirror production. Printing layer-by-layer enables the use of intricate lattices for mass reduction, as well as organic shapes generated by topology optimisation, resulting in mirrors optimised for function as opposed to subtractive machining. However, porosity, a common AM defect, is present in printed aluminium and it is a result of the printing environment being either too hot or too cold, or gas entrapped bubbles within the aluminium powder. When present in an AM mirror substrates, porosity manifests as pits on the reflective surface, which increases micro-roughness and therefore scattered light. There are different strategies to reduce the impact of porosity: elimination during printing, coating the aluminium print in nickel phosphorous, or to apply a heat and pressure treatment to close the pores, commonly known as a hot isostatic press (HIP).
This paper explores the application of HIP on printed aluminium substrates intended for mirror production using single point diamond turning (SPDT). The objective of the HIP is to reduce porosity whilst targeting a small grain growth within the aluminium, which is important in allowing the SPDT to generate surfaces with low micro-roughness. For this study, three disks, 50 mm diameter by 5 mm, were printed in AlSi10Mg at 0 deg, 45 deg, and 90 deg with respect to the build plate. X-ray computed tomography (XCT) was conducted before and after the HIP cycle to confirm the effectiveness of HIP to close porosity. The disks were SPDT and the micro-roughness evaluated. Mechanical testing and electron backscatter diffraction (EBSD) was used to quantify the mechanical strength and the grain size after HIP.
Current browse context:
physics.optics
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
Connected Papers (What is Connected Papers?)
CORE Recommender (What is CORE?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.