Title:Stress induced martensitic transformation in NiTi at elevated temperatures: martensite variant microstructures, recoverable strains and plastic strains
View PDFAbstract:Functional behavior of NiTi shape memory alloys is restricted to temperatures below 150 °C. To shed light on the origin of the loss of functional properties of NiTi with increasing temperature, we have investigated stress induced martensitic transformations in nanocrystalline NiTi shape memory wire by thermomechanical testing supplemented with post-mortem reconstruction of martensite variant microstructures in grains by transmission electron microscopy. It was found that the forward stress induced martensitic transformation proceeding via propagation of macroscopic Luders band fronts in stress plateaus is not completed at the end of the stress plateau and generates unrecoverable plastic strain in addition to recoverable transformation strain. The higher the test temperature, the larger is the plastic strain as well as the volume fraction of retained austenite. The reconstructed martensite variant microstructures in grains of the NiTi wire deformed up to the end of the stress plateau at 120 °C were found to be filled with single domains of (001) compound twin laminate, some grains were nearly detwinned and some grains contained (100) deformation twins. The recoverable transformation strain (~6%) generated by the forward martensitic transformation is nearly independent on the test temperature (plateau stress) because detwinning of (001) compound twins in the microstructure is prohibited by lateral constraint from the surrounding grains in nanocrystalline wire. It is concluded that the gradual loss of functionality of NiTi with increasing temperature does not originate from the plastic deformation of austenite, but that it derives from the lack of resistance of the stress induced martensite to the plastic deformation under increasing stress.
Current browse context:
cond-mat.mtrl-sci
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
Connected Papers (What is Connected Papers?)
CORE Recommender (What is CORE?)
IArxiv Recommender
(What is IArxiv?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.