[Submitted on 7 Jun 2024]
Title:The Effect of Grain Size Distribution on the Defect Generation Mechanism of 0201 Passives
View PDFAbstract:The recent advancements in electronics manufacturing has necessitated the demand for miniaturization of electronic components. In particular, the product sizes for passive components have evolved from 1005 (1.0x0.5mm) which is roughly the size of a grain of sand to 0201 (0.25x0.125mm) which is 1/16th the size of a grain of sand. Grain size distribution and composition play a vital role in tailoring the demands for reliably shrinking dimension of passives. The study focuses on analyzing the effect of grain size and composition, which plays a significant role in maintaining high yield output during the manufacturing processes. The objective of this study is to compare the grain morphology and its effect on defect generation mechanism for 0201 resistors. The experimental setup was prepared to evaluate the grain structure as per ASTM E112-3 test standards. The 0201 resistor samples from three different vendors were assembled on test vehicle PCB (Printed Circuit Board). The resulting observations of the study showed that tombstoning defect was observed during the reflow process for Vendor A. Scanning Electron Microscope (SEM) results showed the presence of microstructural difference in the tin grain size of resistors. The tin grain size for Vendor A was observed to be 2 microns, whereas the grain size for Vendors B and C were 4 and 5 microns, respectively. Furthermore, the results of grain size measurements performed using the intercept method showed that a grain size number of 13 and 13.6 was observed for Vendors B and C, whereas a grain size number of 15 was observed for Vendor A. The second phase of the study focuses on techniques for improving the grain size number to mitigate the tombstoning defect. It was observed that using an alternate plating solution during the manufacturing of passives resulted in decreased grain size number while containing the tombstoning issue.
Current browse context:
cond-mat
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
Connected Papers (What is Connected Papers?)
CORE Recommender (What is CORE?)
IArxiv Recommender
(What is IArxiv?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.