Title:Impact of Resin Molecular Weight on Drying Kinetics and Sag of Coatings
View PDFAbstract:The work herein investigates the impact of resin molecular weight and solvent choice on drying kinetics and sag velocity in polymer films. These films, ranging in thickness from ~60 micrometer to ~120 micrometer were formulated with 45% by weight polymer resin in one of two solvent packages with different relative evaporation rates (RER). Gravimetry was initially used to track drying kinetics and a one-dimensional diffusion model was utilized to compute the apparent solvent diffusivity. In addition, the film thickness was tracked with optical profilometry. Results from these measurements showed that for fixed molecular weight the drying kinetics increased by approximately two-fold for the high RER solvent, whereas the apparent diffusivity tended to increase with increasing polymer molecular weight. Films formulated from higher molecular weight resins had greater initial viscosities and thicknesses for identical draw down blade clearance. By extension, the higher apparent diffusivities at greater molecular weights were attributed to effects of prolonged evaporation times for the thicker films. The sag velocity was measured through the thickness of the film for these systems at a 5 degree incline using the Variable Angle Inspection Microscope (VAIM). Measurements showed an increase in sag velocity for thinner and less viscous films, which was somewhat surprising both because a thinner film will experience lower gravitational stress and quicker drying times as compared to a thicker film. From these data we conclude that formulating a coating with higher molecular weight resin, although likely to increase drying time, will tend to deter sag because of the large impact of viscosity on these phenomena.
Submission history
From: Christopher Wirth [view email][v1] Thu, 28 Mar 2024 16:27:03 UTC (1,979 KB)
Current browse context:
cond-mat.mtrl-sci
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
Connected Papers (What is Connected Papers?)
CORE Recommender (What is CORE?)
IArxiv Recommender
(What is IArxiv?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.