Title:Temperature dependent conductivity, dielectric relaxation, electrical modulus and impedance spectroscopy of Ni substituted Na$_{3+2x}$Zr$_{2-x}$Ni$_{x}$Si$_2$PO$_{\rm 12}$
View PDF HTML (experimental)Abstract:We investigate the structural, dielectric relaxation, electric modulus and impedance behavior of Ni-doped NASICON ceramic Na$_{3+2x}$Zr$_{2-x}$Ni$_{x}$Si$_2$PO$_{\rm 12}$ ($x=$ 0.05--0.2) prepared using the solid-state reaction method. The increase in dielectric constant with temperature and decrease with frequency is explained on the basis of space charge polarization using the two-layer model of Maxwell-Wagner relaxation. The dielectric loss peak at lower temperatures follows the Arrhenius-type behavior with frequency having activation energy of 0.27$\pm$0.01~eV of dipolar relaxation, suggests similar type of defects are responsible for all the doped samples. The real ($\epsilon$ $^{'}$) and imaginary ($\epsilon$ $^{''}$) permittivity variation with frequency shows the broad relaxation behavior indicates the non-Debye type of relaxation in the measured temperature range. The permittivity values decrease with the amount of doping due to the increased number of charge carriers upon Ni doping at the Zr site. The grain contributions are observed at higher frequencies, while grain-boundary contributions occur at the lower side of frequencies. The imaginary part of the electric modulus also shows two types of relaxation peaks for all the samples indicating similar activation energy at low temperatures and variable activation energy at higher temperatures. The fitting of the imaginary modulus using KWW function shows the non-Debye type of relaxation. We find that all modulus curves merge with each other at low temperatures showing a similar type of relaxation, while curves at high temperatures show the dispersed behavior above the peak frequency. The {\it a.c.} conductivity data are fitted using the double power law confirming the grain and grain boundary contributions in total conductivity.
Submission history
From: Rajendra S. Dhaka [view email][v1] Thu, 21 Mar 2024 05:12:02 UTC (3,041 KB)
Current browse context:
cond-mat
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
Connected Papers (What is Connected Papers?)
CORE Recommender (What is CORE?)
IArxiv Recommender
(What is IArxiv?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.