Title:Effect of annealing on the hot salt corrosion resistance of the fine-grained titanium alpha-alloy Ti-2.5Al-2.6Zr obtained via cold Rotary Swaging
View PDFAbstract:A hot salt corrosion (HSC) test was performed on the fine-grained titanium alpha-alloy Ti-2.5Al-2.6Zr (Russian industrial alloy PT-7M). The ultrafine-grained (UFG) microstructure in the titanium alpha-alloy was formed via cold Rotary Swaging. The grain size and volume fraction of the recrystallized microstructure in the alloy were varied by choosing appropriate annealing temperatures and times. The microstructure and corrosion resistance of UFG alloys were studied after 30 min of annealing at 500-700C and after 1000 h of annealing at 250C. Metallographic studies were carried out to investigate the effects of annealing on the nature and extent of corrosive damage in the titanium alpha-alloy Ti-2.5Al-2.6Zr. After HSC tests, surface analyses of the titanium alpha-alloy samples were conducted using X-ray diffraction and electron microscopy. During the HSC testing of the titanium alpha-alloy Ti-2.5Al-2.6Zr, a competitive interaction between intergranular corrosion (IGC) and pitting corrosion was observed. To the best of our knowledge, it was shown for the first time that annealing affects the relationship among the IGC, pitting corrosion and uniform corrosion rates of the titanium alloy. Prolonged low-temperature annealing at 250C resulted in a more pronounced increase in the uniform corrosion rate than short-term high-temperature annealing for 30 min at 500-700C. An in-depth analysis of the effect of the structure and phase composition of the grain boundaries on the susceptibility of the alpha-alloy Ti-2.5Al-2.6Zr to HSC was conducted.
Current browse context:
physics
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
Connected Papers (What is Connected Papers?)
CORE Recommender (What is CORE?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.