Title:Gadolinium scandate by high-pressure sputtering for future generations of high-k dielectrics
View PDFAbstract:Gd-rich gadolinium scandate (Gd2-xScxO3) was deposited by high-pressure sputtering on (100) silicon by alternating the deposition of lower than 0.5 nm thick films of its binary components: Sc2O3 and Gd2O3. The formation of the ternary oxide was observed after the thermal treatments, with a high increase in the effective permittivity of the dielectric (up to 21). The silicon diffuses into the Gd2-xScxO3 films, which show an amorphous character. After the annealing no interfacial silicon oxide is present. CHF-VG curves indicated low hysteresis (55 mV) and a density of interfacial defects of 6e11 eV-1 cm-2.
Current browse context:
cond-mat.mtrl-sci
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
Connected Papers (What is Connected Papers?)
CORE Recommender (What is CORE?)
IArxiv Recommender
(What is IArxiv?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.