Title:Microwave magnetic excitations in U-type hexaferrite Sr$_4$CoZnFe$_{36}$O$_{60}$ ceramics
View PDFAbstract:Microwave (MW) transmission, absorption, and reflection loss spectra of the ferrimagnetic U-type hexaferrite Sr$_4$CoZnFe$_{36}$O$_{60}$ ceramics were studied from 100 MHz to 35 GHz at temperatures between 10 and 390 K. 9 MW magnetic excitations with anomalous behavior near the ferrimagnetic phase transitions were revealed. They also change under the application of weak bias magnetic field (0 - 700 Oe) at room temperature. 6 pure magnetic modes are assigned to dynamics of the magnetic domain walls and inhomogeneous magnetic structure of the ceramics, to the natural ferromagnetic resonance (FMR) and to the higher-frequency magnons. Three modes are considered as the magnetodielectric ones with dominating influence of the magnetic properties on their temperature and field dependences. Presence of the natural FMR in all ferrimagnetic phases proves existence of the non-zero internal magnetization and magnetocrystalline anisotropy. Splitting of the FMR into the two components without magnetic bias was observed in the collinear phase and is attributed to a change of the magnetocrystalline anisotropy during the phase transition. The high-frequency FMR component critically slows down to the phase transition. At room temperature, the FMR splitting and essential suppression of the higher-frequency modes was revealed under the weak bias field (300 - 700 Oe). The highly nonlinear MW response and the FMR splitting are caused by the gradual evolution of the polydomain magnetic structure to a monodomain one. The high number of magnetic excitations observed in the MW region confirms the suitability of using hexaferrite Sr$_4$CoZnFe$_{36}$O$_{60}$ ceramics as MW absorbers, shielding materials and highly tunable filters.
Submission history
From: Dalibor Repček [view email][v1] Tue, 9 Jan 2024 17:08:20 UTC (1,236 KB)
[v2] Tue, 11 Jun 2024 14:31:19 UTC (1,382 KB)
[v3] Wed, 7 Aug 2024 13:41:24 UTC (1,409 KB)
Current browse context:
cond-mat
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
Connected Papers (What is Connected Papers?)
CORE Recommender (What is CORE?)
IArxiv Recommender
(What is IArxiv?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.