Title:Bilayer Vanadium Dioxide Thin Film with Elevated Transition Temperatures and High Resistance Switching
View PDFAbstract:Despite widespread interest in the phase-change applications of vanadium dioxide (VO$_2$), the fabrication of high-quality VO$_2$ thin films with elevated transition temperatures (TIMT) and high Insulator-Metal-Transition resistance switching still remains a challenge. This study introduces a two-step atmospheric oxidation approach to fabricate bilayer VO$_{2-x}$/VO$_2$ films on a c-plane sapphire substrate. To quantify the impact of the VO$_2$ buffer layer, a single-layer VO$_2$ film of the same thickness was also fabricated. The bilayer VO$_{2-x}$/VO$_2$ films wherein the top VO$_{2-x}$ film was under-oxidized demonstrated an elevation in TIMT reaching ~97 $^\circ$C, one of the highest reported to date for VO$_2$ films and is achieved in a doping-free manner. Our results also reveal a one-order increase in resistance switching, with the optimum bilayer VO$_2$/VO$_2$ film exhibiting ~3.6 orders of switching from 25 $^\circ$C to 110 $^\circ$C, compared to the optimum single-layer VO$_2$ reference film. This is accompanied by a one-order decrease in the on-state resistance in its metallic phase. The elevation in TIMT, coupled with increased strain extracted from the XRD characterization of the bilayer film, suggests the possibility of compressive strain along the c-axis. These VO$_{2-x}$/VO$_2$ films also demonstrate a significant change in the slope of their resistance vs temperature curves contrary to the conventional smooth transition. This feature was ascribed to the rutile/monoclinic quasi-heterostructure formed due to the top VO$_{2-x}$ film having a reduced TIMT. Our findings carry significant implications for both the lucid fabrication of VO$_2$ thin film devices as well as the study of phase transitions in correlated oxides.
Submission history
From: Ashok Ponnuchamy [view email][v1] Fri, 29 Dec 2023 02:02:08 UTC (1,392 KB)
Current browse context:
cond-mat.mtrl-sci
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
Connected Papers (What is Connected Papers?)
CORE Recommender (What is CORE?)
IArxiv Recommender
(What is IArxiv?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.