Title:Temperature Dependent Failure of Atomically Thin MoTe2

Abstract:In this study, we systematically investigated the mechanical response of monolayer molybdenum ditelluride (MoTe2) using molecular dynamics simulations. The tensile behavior of the trigonal prismatic phase (2H phase) MoTe2 under uniaxial strain was simulated in both the armchair and zigzag directions. We also investigated the crack formation and propagation in both armchair and zigzag directions at 10K and 300K to understand the fracture behavior of monolayer MoTe2. The crack simulations show clean cleavage for the armchair direction and the cracks were numerous and scattered in the case of the zigzag direction. Finally, we investigated the effect of temperature on Young's modulus and fracture stress of monolayer MoTe2. The results show that at a strain rate of 10^-4 ps^-1, the fracture strength of 2H-MoTe2 in the armchair and zigzag direction at 10K is 16.33 GPa (11.43 N/m) and 13.71429 GPa (9.46 N/m) under a 24% and 18% fracture strain, respectively. The fracture strength of 2H-MoTe2 in the armchair and zigzag direction at 600K is 10.81 GPa (7.56 N/m) and 10.13 GPa (7.09 N/m) under a 12.5% and 12.47% fracture strain, respectively. Although experimental results on MoTe2 are limited for a wide range of temperatures, we have found that Young's modulus agrees with existing literature for pristine MoTe2. For 2H-MoTe2 in both armchair and zigzag directions, the fracture stresses, fracture strengths, and Young's modulus decrease as the temperature rises, resulting from the increased atomic thermal vibrations.