Condensed Matter > Superconductivity
[Submitted on 9 Mar 2023 (v1), last revised 24 Mar 2023 (this version, v3)]
Title:Superconductivity above 70 K observed in lutetium polyhydrides
View PDFAbstract:The binary polyhydrides of heavy rare earth lutetium that shares a similar valence electron configuration to lanthanum have been experimentally discovered to be superconductive. The lutetium polyhydrides were successfully synthesized at high pressure and high temperature conditions using a diamond anvil cell in combinations with the in-situ high pressure laser heating technique. The resistance measurements as a function of temperature were performed at the same pressure of synthesis in order to study the transitions of superconductivity (SC). The superconducting transition with a maximum onset temperature (Tc) 71 K was observed at pressure of 218 GPa in the experiments. The Tc decreased to 65 K when pressure was at 181 GPa. From the evolution of SC at applied magnetic fields, the upper critical field at zero temperature {\mu}0Hc2(0) was obtained to be ~36 Tesla. The in-situ high pressure X-ray diffraction experiments imply that the high Tc SC should arise from the Lu4H23 phase with Pm-3n symmetry that forms a new type of hydrogen cage framework different from those reported for previous light rare earth polyhydride superconductors.
Submission history
From: Xiancheng Wang [view email][v1] Thu, 9 Mar 2023 08:54:08 UTC (412 KB)
[v2] Wed, 22 Mar 2023 11:54:27 UTC (913 KB)
[v3] Fri, 24 Mar 2023 11:26:02 UTC (913 KB)
Current browse context:
cond-mat.str-el
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
Connected Papers (What is Connected Papers?)
CORE Recommender (What is CORE?)
IArxiv Recommender
(What is IArxiv?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.