Title:High temperature dielectric and impedance spectroscopy study of LaCo$_{0.7}$Nb$_{0.3}$O$_3$
View PDFAbstract:We report the high temperature dielectric and {\it ac} impedance spectroscopy investigation of Nb substituted LaCo$_{0.7}$Nb$_{0.3}$O$_3$ polycrystalline sample. The maximum dielectric constant value was observed $\approx$1400 at around 400~K where the peak value shows a decreasing trend at higher temperatures and frequency. Similar variation was reflected in the dielectric loss (tan$\delta$) behavior with temperature, which shows the thermal activation of the charge carriers in the material. The analysis of high temperature impedance spectroscopy data shows the grain and grain boundary contributions by fitting the Nyquist plots to the equivalent circuit. From the analysis of the impedance and modulus spectra, it was possible to discern between the effects of overlapping grains, grain boundaries, and electrode interfaces. The relaxation time decreases with an increase in the temperature and the activation energy changes from 0.44~eV to 0.56~eV at around 400~K, which is due to involvement of thermal activation in the conduction of charge carriers. The conductivity is found to be increased with temperature for a given frequency, which again shows the semiconducting behavior. Whereas the conductivity increases with increase in frequency at lower temperatures. Also, the conductivity almost saturates with frequency at high temperatures.
Submission history
From: Rajendra S. Dhaka [view email][v1] Tue, 16 Aug 2022 04:58:33 UTC (2,071 KB)
Current browse context:
cond-mat.mtrl-sci
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
Connected Papers (What is Connected Papers?)
CORE Recommender (What is CORE?)
IArxiv Recommender
(What is IArxiv?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.