Title:Mass spectrometric investigations into 3D printed parts to assess radiopurity as ultralow background materials for rare event physics detectors
View PDFAbstract:New data are reported for polyvinylidene fluoride (PVDF), polyphenylene sulfide (PPS), and two forms of polyetherimide (PEI, branded ULTEM 1010 and 9085). Data for starting filaments and both simple and complex printed parts are reported. PVDF filaments and simple printed beads, were found to have values of approximately 30 and 50 ppt for Th-232 and U-238, respectively, while a more complex spring clip part had slightly elevated Th-232 levels of 65 ppt, with U-238 remaining at 50 ppt. PPS filament was found to have concentrations of 270 and 710 ppt for Th-232 and U-238, respectively, and were not chosen to be printed as those levels were already higher than other material options. ULTEM 1010 filaments and printed complex spring clip parts were found to have concentrations of around 5 and 7 ppt for Th-232 and U-238, respectively, illustrating no significant contamination from the printing process. ULTEM 9085 filaments were found to have concentrations of around 9 and 5 ppt for Th-232 and U-238, respectively, while the printed complex spring clip part was found to have slightly elevated concentrations of 25 and 7 ppt for Th-232 and U-238, respectively. These results were all obtained using a novel dry ashing method in crucibles constructed of ultralow background electroformed copper or, when applicable, microwave-assisted wet ashing digestion. Samples and process blanks were spiked with Th-229 and U-233 as internal standards prior to dry/wet ashing and determinations were made by inductively coupled plasma mass spectrometry (ICP-MS). In order to maintain high radiopurity levels, pre-cleaning the filaments before printing and post-cleaning the parts is recommended, although the printing process itself has shown to contribute very minute amounts of radiocontaminants.
Current browse context:
physics.ins-det
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Connected Papers (What is Connected Papers?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
alphaXiv (What is alphaXiv?)
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Hugging Face (What is Huggingface?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
CORE Recommender (What is CORE?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.