Title:Impact of hydrogen on the dislocation structure upon tensile loading in a high manganese twinning induced plasticity steel

Abstract:High-manganese twinning-induced plasticity (TWIP) steels exhibit mechanical properties making them attractive for structural applications. However, they are prone to hydrogen embrittlement (HE), and may undergo a brittle, catastrophic failure upon hydrogen ingress in service conditions. We investigated the he susceptibility of a Fe28Mn0.3C (wt.%) TWIP steel. We observed a reduction in engineering strain from 75% to 10% and a 20% increase in yield strength following the hydrogen-charging. The microstructural evolution was examined at three different, lower tensile strain levels, i. E. , 3%, 5% and 7% by using correlative electron backscatter diffraction (EBSD) and electron channeling contrast imaging (ECCI). At 3% strain, dislocation cells form in the hydrogen-charged region, which can be attributed to the increased yield strength that promotes the slip activation on multiple slip systems. We introduce an approach for image processing to quantify the cell size. At 7% strain, we observed the formation of stacking faults and hexagonal close packed -martensite in the hydrogen-charged region due to the reduction in stacking fault energy (SFE) associated to the presence of hydrogen. In contrast, the microstructure of the uncharged samples was composed of planar dislocation arrangements at 3%, 5% and 7% strain, which is indicative of planar slip. We discuss the details of how hydrogen modifies the dislocation structures and the overall deformation mechanism, and the present study is expected to facilitate the future design of steels resistant to HE.