Title:Superconductivity enhanced in the polar metal region of Sr$_{0.95}$Ba$_{0.05}$TiO$_3$ and Sr$_{0.985}$Ca$_{0.015}$TiO$_3$ revealed by the systematic Nb doping

Abstract:Different ferroelectrics, Sr$_{0.95}$Ba$_{0.05}$TiO$_3$ and Sr$_{0.985}$Ca$_{0.015}$TiO$_3$, turn into metallic with centrosymmetry breaking by the electron doping. The systematic substitution of Nb$^{5+}$ for Ti$^{4+}$ has revealed that the two polar metals commonly exhibit a simple superconducting dome with a single convex. Interestingly, the superconducting transition temperature $T_{\mathrm{c}}$ is more enhanced in these polar metals compared with the non-polar matrix Sr(Ti,Nb)O$_3$ . The maximum $T_{\mathrm{c}}$ reaches 0.75\,K, the highest in the families of SrTiO$_3$ ever reported. However, the $T_{\mathrm{c}}$ enhancement is unexpectedly lower in the vicinity of the ferroelectric quantum critical point (QCP). It becomes much more prominent by further going into the dilute carrier-density region, where the screening is less effective. The results suggest that the centrosymmetry breaking, i.e., the ferroelectric nature, does not kill the superconductivity. It rather directly enhances the superconductivity without the help of quantum fluctuation.