Title:High-field magnetoresistance of microcrystalline and nanocrystalline Ni metal at 3 K and 300 K
View PDFAbstract:The magnetoresistance (MR) and the magnetization isotherms were studied up to high magnetic fields at T = 3 K and 300 K for a microcrystalline ($\mu$c) Ni foil corresponding to bulk Ni and for a nanocrystalline (nc) Ni foil. At T = 3 K, for the $\mu$c-Ni sample with a residual resistivity ratio (RRR) of 331, the field dependence of the resistivity was similar to what was reported previously for high-purity ferromagnets whereas the MR(H) behavior for the nc-Ni sample with RRR = 9 resembled that what was observed at low temperatures for Ni-based alloys with low impurity concentration. In the magnetically saturated state, the resistivity increased with magnetic field for both samples at T = 3 K and the field dependence was dominated by the ordinary MR due to the Lorentz force acting on the electron trajectories. However, the MR(H) curves were found to be saturating for $\mu$c-Ni and non-saturating for nc-Ni, the difference arising from their very different electron mean free paths. At T = 300 K, the MR(H) curves of both Ni samples were very similar to those known for bulk Ni. After magnetic saturation, the resistivity decreased nearly linearly with magnetic field which behavior is due to the suppression of thermally-induced magnetic disorder with increasing magnetic field. The MR(H) data were analyzed at both temperatures with the help of Kohler plots from which the resistivity anisotropy splitting ($\Delta\rho_{AMR}$) and the anisotropic magnetoresistance (AMR) ratio were derived. It was demonstrated that at T = 300 K, $\rho(H\rightarrow 0)=\rho(B\rightarrow 0)$ due to the negligible contribution of the ordinary MR. The data for the two Ni samples at 3 K and 300 K were found to indicate an approximately linear scaling of $\Delta\rho_{AMR}$ with the zero-field resistivity. This implies that the AMR ratio does not vary significantly with temperature in either microstructural state of Ni.
Submission history
From: Krisztian Palotas [view email][v1] Tue, 22 Mar 2022 09:45:03 UTC (1,125 KB)
Current browse context:
cond-mat
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
Connected Papers (What is Connected Papers?)
CORE Recommender (What is CORE?)
IArxiv Recommender
(What is IArxiv?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.