Title:A15 Nb$_3$Si -- A "high" Tc superconductor synthesized at a pressure of one megabar and metastable at ambient conditions
View PDFAbstract:A15 Nb$_3$Si is, until now, the only high temperature superconductor produced at high pressure (~110 GPa) that has been successfully brought back to room pressure conditions in a metastable condition. Based on the current great interest in trying to create metastable-at-room-pressure high temperature superconductors produced at high pressure, we have restudied explosively compressed A15 Nb$_3$Si and its production from tetragonal Nb$_3$Si. First, diamond anvil cell pressure measurements up to 88 GPa were performed on explosively compressed A15 Nb$_3$Si material to trace Tc as a function of pressure. Tc is suppressed to ~ 5.2 K at 88 GPa. Then, using these Tc (P) data for A15 Nb$_3$Si, pressures up to 92 GPa were applied at room temperature (which increased to 120 GPa at 5 K) on tetragonal Nb$_3$Si. Measurements of the resistivity gave no indication of any A15 structure production, i.e., no indications of the superconductivity characteristic of A15 Nb$_3$Si. This is in contrast to the explosive compression (up to P~110 GPa) of tetragonal Nb$_3$Si, which produced 50-70% A15 material, Tc = 18 K at ambient pressure, in a 1981 Los Alamos National Laboratory experiment. Our theoretical calculations show that A15 Nb$_3$Si has an enthalpy vs the tetragonal structure that is 0.07 eV/atom smaller at 100 GPa, implying that the accompanying high temperature (1000 deg C) caused by explosive compression is necessary to successfully drive the reaction kinetics of the tetragonal -> A15 Nb$_3$Si structural transformation. Annealing experiments on the A15 explosively compressed material reaching time scales of 39 years are consistent with this viewpoint.
Submission history
From: G. R. Stewart [view email][v1] Sat, 5 Dec 2020 00:20:18 UTC (938 KB)
[v2] Sat, 5 Jun 2021 02:32:20 UTC (717 KB)
Current browse context:
cond-mat.supr-con
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Connected Papers (What is Connected Papers?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
alphaXiv (What is alphaXiv?)
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Hugging Face (What is Huggingface?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
CORE Recommender (What is CORE?)
IArxiv Recommender
(What is IArxiv?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.