Title:UV/Near-IR dual band photodetector based on p-GaN/α-In2Se3 heterojunction
View PDFAbstract:In this report, we demonstrate dual band vertical heterojunction photodetector realized by integrating {\alpha}-In2Se3 with p-type GaN. Flakes of ~ 110 nm thickness were exfoliated on MOCVD grown p-GaN on silicon substrate. Devices showed two distinct detection peaks in spectral responsivity, one at 365 nm and another at 850 nm, corresponding to band edges of GaN and {\alpha}-In2Se3 respectively, with considerable rejection in visible spectrum. Normalised responsivity values were found out to be ~70 mA/W at both 365 nm and 850 nm for the bias of -3V along with photo-to-dark current ratio of ~665 and ~75 in that order. The Devices also showed fast transient response with no persistent photoconductivity (PPC). The specific detectivity values estimated were ~10^11 Jones and ~10^10 Jones corresponding to illumination at 365 nm and 850 nm respectively. A good linearity of ~0.4 was observed in power dependent analysis of spectral responsivity at 365 nm. The device performance, post annealing was also studied. This study is expected to pave way for new type of optoelectronic devices by integrating direct bandgap layered material like {\alpha}-In2Se3 and wide bandgap semiconductors.
Current browse context:
physics.app-ph
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Connected Papers (What is Connected Papers?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
alphaXiv (What is alphaXiv?)
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Hugging Face (What is Huggingface?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
CORE Recommender (What is CORE?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.