Title:Temperature Dependence of Sensitivity of 2DEG-Based Hall-Effect Sensors
View PDFAbstract:The magnetic sensitivity of Hall-effect sensors made of InAlN/GaN and AlGaN/GaN heterostructures was measured between room temperature and 576°C. Both devices showed decreasing voltage-scaled magnetic sensitivity at high temperature, declining from 53 to 8.3 mV/V/T for the InAlN/GaN sample and from 89 to 8.5 mV/V/T for the AlGaN/GaN sample, corresponding to the decreasing electron mobility due to scattering effects at elevated temperatures. Alternatively, current-scaled sensitivities remained stable over the temperature range, only varying by 13.1% from the mean of 26.3 V/A/T and 10.5% from the mean of 60.2 V/A/T for the InAlN/GaN and AlGaN/GaN samples respectively. This is due to the minimal temperature dependence of the electron sheet density on the 2-dimensional electron gas (2DEG). Both devices showed consistency in their voltage- and current-scaled sensitivity over multiple temperature cycles as well as nearly full recovery when returned to room temperature after thermal cycling. Additionally, an AlGaN/GaN sample held at 576°C for 12 hours also showed nearly full recovery at room temperature, further suggesting that GaN-based Hall-effect sensors are a good candidate for use in high temperature applications.
Current browse context:
physics.ins-det
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
Connected Papers (What is Connected Papers?)
CORE Recommender (What is CORE?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.