Title:Beneficial influence of Hf and Zr additions to Nb4at.%Ta on the vortex pinning of Nb$_{3}$Sn with and without an O source
View PDFAbstract:Here we show that addition of Hf to Nb4Ta can significantly improve the high field performance of Nb$_{3}$Sn, making it suitable for dipole magnets for Future Circular Collider (FCC). A big challenge for the FCC is that a realistic production target for FCC Nb3Sn requires ~30% improvement over current conductor performance. Recent success with internal oxidation(IO) of Nb-Zr precursor has shown significant improvement in the layer J$_{c}$ of Nb$_{3}$Sn wires, albeit the complication of providing an internal O$_{2}$ diffusion path and avoiding degradation of irreversibility field($_{irr}$). We compare Zr and Hf additions to the standard Nb4Ta alloy of maximum H$_{c2}$ and H$_{irr}$. Nb4Ta rods with 1Zr or 1Hf were made into monofilament wires with and without SnO$_{2}$ and their properties measured over the entire superconducting range up to 31 T. We found that group IV alloying of Nb4Ta raises H$_{irr}$, though adding O$_{2}$ still degrades this slightly. As noted in Nb1Zr studies, the pinning force density F$_{p}$ is strongly enhanced and its peak value shifted to higher field by IO. A surprising result of this work is that we found better properties in Nb4Ta1Hf without SnO$_{2}$, F$_{pmax}$ achieving 2.35 times that of the standard Nb4Ta alloy, while the oxidized Nb4Ta1Zr alloy achieved 1.54 times that of the Nb4Ta alloy. The highest layer J$_{c}$ (16 T, 4.2 K) of 3700 A/mm$^{2}$ was found in the SnO$_{2}$-free wire made with Nb4Ta1Hf alloy. Using a standard A15 cross-section fraction of 60% for modern PIT and RRP wires, we estimated that a non-Cu J$_{c}$ of 2200 A/mm$^{2}$ is obtainable in modern conductors, well above the 1500A/mm$^{2}$ FCC specification. Moreover, the best properties were obtained without SnO$_{2}$, the Nb4Ta1Hf alloy appears to open a straightforward route to enhanced properties in Nb$_{3}$Sn wires.
Submission history
From: Shreyas Balachandran [view email][v1] Wed, 21 Nov 2018 18:26:32 UTC (899 KB)
Current browse context:
cond-mat.supr-con
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
Connected Papers (What is Connected Papers?)
CORE Recommender (What is CORE?)
IArxiv Recommender
(What is IArxiv?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.