Title:Electrical and Optical Properties of Heavily Ge-Doped AlGaN
View PDFAbstract:We report the effect of germanium as n-type dopant on the electrical and optical properties of AlxGa1-xN layers grown by plasma assisted molecular-beam epitaxy. The Al content has been varied from x = 0 to 0.66, confirmed by Rutherford backscattering spectrometry, and the Ge concentration was increased up to [Ge] = 1E21 cm-3. Even at these high doping levels Ge does not induce any structural degradation in AlxGa1-xN layers with x below 0.15. However, for higher Al compositions, clustering of Ge forming crystallites were observed. Hall effect measurements show a gradual decrease of the carrier concentration when increasing the Al mole fraction, which is already noticeable in samples with x = 0.24. Samples with x = 0.64-0.66 remain conductive, but the donor activation rate drops to around 0.1% (carrier concentration around 1E18 cm-3 for [Ge] = 1E21 cm-3). From the optical point of view, the low temperature photoluminescence is dominated by the band-to-band emission, which show only spectral shift and broadening associated to the Burstein-Moss effect. The evolution of the photoluminescence peak position with temperature shows that the free carriers due to Ge doping can efficiently screen the potential fluctuations induced by alloy disorder.
Submission history
From: Eva Monroy [view email][v1] Thu, 25 Oct 2018 21:05:04 UTC (1,128 KB)
[v2] Thu, 8 Nov 2018 15:56:54 UTC (1,141 KB)
[v3] Thu, 13 Dec 2018 11:41:48 UTC (1,127 KB)
Current browse context:
cond-mat.mtrl-sci
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
Connected Papers (What is Connected Papers?)
CORE Recommender (What is CORE?)
IArxiv Recommender
(What is IArxiv?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.