Title:Ternary Nb3Sn superconductors with artificial pinning centers and high upper critical fields
View PDFAbstract:In this letter we demonstrate the development of ternary Nb3Sn multifilamentary conductors with artificial pinning centers (APC) which achieve high critical fields. These recently-developed conductors were tested in a 31 T magnet, and the results showed that their upper critical field (Bc2) values at 4.2 K are 27-28 T, and irreversible field (Birr) values are above 26 T, values similar to or higher than those of best RRP conductors. The non-Cu Jc has been brought to nearly 1200 A/mm2 at 16 T and 4.2 K, comparable to RRP, in spite of the fact that the fine-grain Nb3Sn fractions in filaments are still low (20-30%) and the grain sizes are still not fully refined (70-80 nm) due to conductor designs and heat treatments that are not yet optimized. The Nb3Sn layer Jc at 4.2 K, 16 T is 4710 A/mm2 for the APC wire with 1%Zr, about 2.5 times higher than RRP conductors, in spite of the fact that its grain size is not yet fully refined due to insufficient oxygen and unoptimized heat treatment. An analysis is presented about the non-Cu Jc that can be achieved by further optimizing the APC conductors and their heat treatments.
Submission history
From: Xingchen Xu [view email][v1] Wed, 24 Oct 2018 18:25:13 UTC (624 KB)
[v2] Tue, 27 Nov 2018 06:00:49 UTC (680 KB)
[v3] Wed, 28 Nov 2018 15:52:59 UTC (638 KB)
Current browse context:
cond-mat
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
Connected Papers (What is Connected Papers?)
CORE Recommender (What is CORE?)
IArxiv Recommender
(What is IArxiv?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.