Title:Synchrotron X-ray tomography investigation of 3D morphology of intermetallic phases and pores and their effect on the mechanical properties of cast Al-Cu alloys
View PDFAbstract:The influence of Fe content on the three-dimensional (3D) morphology of Fe-rich intermetallic phases (Fe phases), Al2Cu, and pores and mechanical properties of cast Al-5.0Cu-0.6Mn alloys with 0.5 and 1.0 wt. % Fe are characterized using synchrotron X-ray tomography and a tensile test. The results show that both Fe phases and Al2Cu exhibit a complex 3D network structure, and the pores are irregular with complex interconnected and near-globular shape. As the Fe content increases from 0.5 % to 1.0 %, the volume fraction and equivalent diameter of Fe phases decrease, whereas both their interconnectivities decrease. Skeletonization analysis shows that the Chinese-script-shaped Fe phase is compacted than the plate-like Fe phases. The equivalent diameter and sphericity of pores vary with Fe content, and their relationships follow exponential functions, Y = 7.14*X-1.29 and Y = 7.06*X-1.20, respectively. The addition of Fe results in a decrease in the ultimate tensile strength and elongation from 223.7 MPa to 199.8 MPa and from 5.51 % to 3.64 %, respectively, owing to increasing volume fraction of sharp-edged Fe phases and pores, resulting in stress concentration during tensile test.
Current browse context:
cond-mat.mtrl-sci
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
Connected Papers (What is Connected Papers?)
CORE Recommender (What is CORE?)
IArxiv Recommender
(What is IArxiv?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.