Condensed Matter > Superconductivity
This paper has been withdrawn by Zongqing Ma
[Submitted on 27 Nov 2015 (v1), last revised 24 Mar 2017 (this version, v2)]
Title:Transition from insulator to superconductor and significant enhancement of superconductivity in FeSe films via tuning Fe-vacancy disorders
No PDF available, click to view other formatsAbstract:In contrast to its bulk crystals, the FeSe film or layer exhibits better superconductivity performance, which attract much interest in its fundamental research as well as potential application. In present work, transition from insulator to superconductor and significant enhancement of superconductivity were achieved in the high quality (00l) oriented FeSe films via controlling the thickness as well as the Fe/Se ratio. The highest Tc up to 15.2 K (almost 2 times higher than those of bulk crystals) and Hc2 up to 35.5 T are obtained in our atmosphere-stable FeSe thin film with practical thickness (240 nm), implying their great potential application in the electronic devices at high magnetic fields. More importantly, it was found that the Fe-vacancy disorder in FeSe films is the intrinsic factor determining the evolution of the superconductivity, rather than thickness effect. In our non-superconducting FeSe film with Fe/Se ratio of 1.00:1.09, insulating \b{eta}-Fe1-xSe phase with iron-vacancy disorders is the main phase and more likely to be the parent phase of FeSe superconducting system. Tuning the Fe-vacancy disorders via changing the Fe/Se ratio can dramatically vary the concentration of charge carrier and introduce proper electron doping, which finally leads to the transition from insulator to superconductor and further enhancement in the superconductivity. Intriguingly, our results also indicate that when the Fe/Se ratio of film is beyond a critical value, superconducting FeSe films will become instable, and phase separation occurs with new non-superconducting phase precipitating in the superconducting matrix, causing the degradation in the superconductivity. The results in present work help us to well understand the intrinsic mechanism of superconductivity among Fe-Se superconducting system and provide a new strategy to further pursue higher Tc in these materials.
Submission history
From: Zongqing Ma [view email][v1] Fri, 27 Nov 2015 13:29:00 UTC (834 KB)
[v2] Fri, 24 Mar 2017 10:11:38 UTC (1 KB) (withdrawn)
Current browse context:
cond-mat.supr-con
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Connected Papers (What is Connected Papers?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
alphaXiv (What is alphaXiv?)
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Hugging Face (What is Huggingface?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
CORE Recommender (What is CORE?)
IArxiv Recommender
(What is IArxiv?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.