Title:Enhanced Raman scattering and weak localization in graphene deposited on GaN nanowires
View PDFAbstract:The influence of GaN nanowires on the optical and electrical properties of graphene deposited on them was studied using Raman spectroscopy and microwave induced electron transport method. It was found that interaction with the nanowires induces spectral changes as well as large enhancement of Raman scattering intensity. Surprisingly, the smallest enhancement (about 30-fold) was observed for the defect induced D' process and the highest intensity increase (over 50-fold) was found for the 2D transition. The observed energy shifts of the G and 2D bands allowed to determine carrier concentration fluctuations induced by GaN nanowires. Comparison of Raman scattering spatial intensity maps and the images obtained using scanning electron microscope led to conclusion that vertically aligned GaN nanowires induce a homogenous strain, substantial spatial modulation of carrier concentration in graphene and unexpected homogenous distribution of defects created by interaction with nanowires. The analysis of the D and D' peak intensity ratio showed that interaction with nanowires also changes the probability of scattering on different types of defects. The Raman studies were correlated with weak localization effect measured using microwave induced contactless electron transport. Temperature dependence of weak localization signal showed electron-electron scattering as a main decoherence mechanism with additional, temperature independent scattering reducing coherence length. We attributed it to the interaction of electrons in graphene with charges present on the top of nanowires due to spontaneous and piezoelectric polarization of GaN. Thus, nanowires act as antennas and generate enhanced near field which can explain the observed large enhancement of Raman scattering intensity.
Submission history
From: Jakub Kierdaszuk [view email][v1] Sun, 31 May 2015 11:36:01 UTC (2,168 KB)
[v2] Sun, 20 Sep 2015 21:04:54 UTC (2,107 KB)
[v3] Thu, 24 Sep 2015 19:35:20 UTC (1,689 KB)
Current browse context:
cond-mat.mes-hall
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Connected Papers (What is Connected Papers?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
alphaXiv (What is alphaXiv?)
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Hugging Face (What is Huggingface?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
CORE Recommender (What is CORE?)
IArxiv Recommender
(What is IArxiv?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.