Title:Magnetocaloric properties of LaFe$_{13-x-y}$Co$_x$Si$_y$ and commercial grade Gd
View PDFAbstract:The magnetocaloric properties of three samples of LaFe$_{13-x-y}$Co$_x$Si$_y$ have been measured and compared to measurements of commercial grade Gd. The samples have (x=0.86, y=1.08), (x=0.94, y=1.01) and (x=0.97, y=1.07) yielding Curie temperatures in the range 276-288 K. The magnetization, specific heat capacity and adiabatic temperature change have been measured over a broad temperature interval. Importantly, all measurements were corrected for demagnetization, allowing the data to be directly compared. In an internal field of 1 T the maximum specific entropy changes were 6.2, 5.1 and 5.0 J/kg K, the specific heat capacities were 910, 840 and 835 J/kg K and the adiabatic temperature changes were 2.3, 2.1 and 2.1 K for the three LaFeCoSi samples respectively. For Gd in an internal field of 1 T the maximum specific entropy change was 3.1 J/kg K, the specific heat capacity was 340 J/kg K and the adiabatic temperature change was 3.3 K. The adiabatic temperature change was also calculated from the measured values of the specific heat capacity and specific magnetization and compared to the directly measured values. In general an excellent agreement was seen.
Current browse context:
cond-mat.mtrl-sci
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
Connected Papers (What is Connected Papers?)
CORE Recommender (What is CORE?)
IArxiv Recommender
(What is IArxiv?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.