Title:Fabrication and modeling of piezoelectric transducers for High-Frequency medical imaging
View PDFAbstract:We have studied the processing of piezoelectric thick films using electrophoretic deposition (EPD) for high-frequency ultrasound applications. Lead-zirconium-titanate (PZT) particles synthetized by solid states synthesis were dispersed in ethanol using ammonium polyacrylate (PAA). The electrophoretic deposition of PZT particles was performed at a constant-current mode. PZT thick-films deposited at 1 mA for 60 seconds were sintered at 900oC for 2 hours in a PbO-controlled atmosphere. The scanning-electron microscopy (SEM) analysis shows that the thickness of PZT layer is uniform and that the pores are homogeneously distributed within the layer. The complex electrical impedance was measured and fitted by KLM scheme in order to deduce the dielectric, mechanical and piezoelectric parameters of the thick-films. The density and thickness of PZT thick films are used as inputs and the thickness coupling factor kt, dielectric constant at constant strain and resonant frequency are deduced. The results show that homogeneous PZT thick-film structures with tailored thickness and density prepared by EPD and sintering having a resonant frequency around 20 MHz can be used for noninvasive medical ultrasound imaging and diagnostics.
Submission history
From: Andre-Pierre Abellard [view email] [via CCSD proxy][v1] Wed, 24 Apr 2013 16:27:56 UTC (515 KB)
Current browse context:
physics.med-ph
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
Connected Papers (What is Connected Papers?)
CORE Recommender (What is CORE?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.