Title:Epitaxial (111) Films of Cu, Ni, and Cu$_xNi$_y$ on α-Al$_2$O$_3$(0001) for Graphene Growth by Chemical Vapor Deposition
View PDFAbstract:Films of (111)-textured Cu, Ni, and Cu$_x$Ni$_y$ were evaluated as substrates for chemical vapor deposition of graphene. A metal thickness of 400 nm to 700 nm was sputtered onto a substrate of $\alpha-$Al$_2$O$_3$(0001) at temperatures of 250 C to 650 C. The films were then annealed at 1000 C in a tube furnace. X-ray and electron backscatter diffraction measurements showed all films have (111) texture but have grains with in-plane orientations differing by $60^{\circ}$. The in-plane epitaxial relationship for all films was $[110]_{metal}$||$[10\bar{1}0]_{{Al}_{2}{O}_{3}}$. Reactive sputtering of Al in O$_2$ before metal deposition resulted in a single in-plane orientation over 97 % of the Ni film but had no significant effect on the Cu grain structure. Transmission electron microscopy showed a clean Ni/Al$_2$O$_3$ interface, confirmed the epitaxial relationship, and showed that formation of the $60^{\circ}$ twin grains was associated with features on the Al$_2$O$_3$ surface. Increasing total pressure and Cu vapor pressure during annealing decreased the roughness of Cu and and Cu$_x$Ni$_y$ films. Graphene grown on the Ni(111) films was more uniform than that grown on polycrystalline Ni/SiO$_2$ films, but still showed thickness variations on a much smaller length scale than the distance between grains.
Current browse context:
cond-mat.mtrl-sci
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
Connected Papers (What is Connected Papers?)
CORE Recommender (What is CORE?)
IArxiv Recommender
(What is IArxiv?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.