Condensed Matter > Strongly Correlated Electrons
[Submitted on 28 Feb 2012]
Title:Magnetization study to probe the effect of N2+ irradiation on Fe/Co bilayers
View PDFAbstract:Fe/Co bilayers were made using ion beam sputtering and then were subjected to nitrogen-ion irradiation to explore the influence of irradiation on their magnetic properties. Magnetization studies of Fe/Co bilayers along with their irradiated counterparts were then performed. The magnetization and coercivity of the as-deposited sample exhibited a two-fold uniaxial symmetry while the behavior for high temperature irradiated sample depicts a small shift in the two fold behavior. The magnetization data measured with the magnetic field perpendicular to the plane of the film exhibited a hysteresis in both the case of the irradiated sample as well as as-deposited sample. A small increase in coercivity for the irradiated sample was observed which is due to various reasons including formation of FeCo solid solution due to ion irradiation at the interface.
Current browse context:
cond-mat.str-el
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
Connected Papers (What is Connected Papers?)
CORE Recommender (What is CORE?)
IArxiv Recommender
(What is IArxiv?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.