Title:Phonon softening and "forbidden" mode observed by Raman scattering in Na0.5CoO2
View PDFAbstract: Polarized Raman scattering measurements have been performed on Na0.5CoO2 single crystal from 8 to 305 K. Both the A1g and E1g phonon modes show a softening below Tc1 ~ 83 K. Additionally, the A1g phonon mode, which is forbidden in the scattering geometry of cross polarization for the triangular CoO2 layers, appears below Tc1. In contrast, the metal-insulator transition at Tc2 ~ 46 K has only secondary effect on the Raman spectra. The phonon softening and the ``forbidden'' Raman intensity follow closely magnetic order parameter and the gap function at the Fermi surface, indicating that the distortion of CoO6 octahedra at Tc1, instead of the Na ordering at ~350 K, is the relevant structural component of the 83 K phase transition.
Current browse context:
cond-mat.supr-con
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
Connected Papers (What is Connected Papers?)
CORE Recommender (What is CORE?)
IArxiv Recommender
(What is IArxiv?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.